A study of electrospun nanofibers and diatomaceous earth materials for the extraction of alkaloids, flavonoids and aromatic amines in various matrices
- Mothibedi, Kediemetse (Kedimetse)
- Authors: Mothibedi, Kediemetse (Kedimetse)
- Date: 2013 , 2013-04-07
- Subjects: Nanofibers , Electrospinning , Sorbents , Extraction (Chemistry) , Alkaloids , Flavonoids , Amines , Matrices , Goldenseal , Ginkgo , Dyes and dyeing -- Chemistry
- Language: English
- Type: Thesis , Masters , MSc
- Identifier: vital:4288 , http://hdl.handle.net/10962/d1003052 , Nanofibers , Electrospinning , Sorbents , Extraction (Chemistry) , Alkaloids , Flavonoids , Amines , Matrices , Goldenseal , Ginkgo , Dyes and dyeing -- Chemistry
- Description: The thesis explored the use of different sorbent materials in solid phase extraction method development. The methods included the use of the polymeric Agilent Bond Elut Plexa solid phase extraction and electrospun polymer-silica composite sorbents for clean-up and preconcentration. Sample clean-up for alkaloids (hydrastine and berberine) in goldenseal, Hydrastis canadensis and flavonoids (quercetin, kaempferol and isorhamnetin) in Ginkgo biloba was achieved using Bond Elut Plexa SPE sorbent. Clean-up of flavonoids in Ginkgo biloba was also achieved using electrospun polymer-silica composite (polystyrene-silica, polyacrylonitrile-silica and nylon 6-silica) sorbents. All analysis of flavonoids and alkaloids was carried out using an Agilent 1200 Series HPLC coupled with a diode array detector. Good peak separation was achieved in less than 6 min employing an Agilent ZORBAX Eclipse Plus C18 column (4.6 x 75 mm, 3.5 μm) at 35⁰C. The mobile phases employed were 0.1% phosphoric acid/methanol gradient and 0.5% phosphoric acid/methanol (40:60) for alkaloids and flavonoids respectively. The calibration curves exhibited linearity up to 120 μg mL⁻¹ with correlation coefficients of more than 0.9980. The recoveries ranged from 73-109% with relative standard deviation of less than 5% for all analytes. Agilent Chem Elut supported liquid extraction was employed for the development of a sample preparation method for the determination of 24 banned aromatic amines from azo dyes in textile following the EU standard method EN 14362-1:2003 (E) and the Chinese standard method GB/T 17592-2006. The supported liquid extraction was effective in the extraction of the aromatic amines from textile (cotton, wool and polyester/cotton [80%:20%]). Most of the recoveries obtained were conforming to the minimum requirements set in the EN 14362-1:2003 (E) standard method and the relative standard deviations were less than 15%. Good peak separation was obtained within 70 min run time using the Agilent Zorbax SB-Phenyl column (4.6 mm x 250 mm, 5-micron) or the Agilent DB-35 MS (J & W) (30 m x 0.25 mm, 0.25 μm film thickness. It was demonstrated that the polymeric Agilent Bond Elut Plexa, electrospun nanofibers and diatomaceous earth were effective in extraction of alkaloids, flavonoids and aromatic amines in different matrices. The developed methods were simple, rapid and reproducible.
- Full Text:
- Date Issued: 2013
- Authors: Mothibedi, Kediemetse (Kedimetse)
- Date: 2013 , 2013-04-07
- Subjects: Nanofibers , Electrospinning , Sorbents , Extraction (Chemistry) , Alkaloids , Flavonoids , Amines , Matrices , Goldenseal , Ginkgo , Dyes and dyeing -- Chemistry
- Language: English
- Type: Thesis , Masters , MSc
- Identifier: vital:4288 , http://hdl.handle.net/10962/d1003052 , Nanofibers , Electrospinning , Sorbents , Extraction (Chemistry) , Alkaloids , Flavonoids , Amines , Matrices , Goldenseal , Ginkgo , Dyes and dyeing -- Chemistry
- Description: The thesis explored the use of different sorbent materials in solid phase extraction method development. The methods included the use of the polymeric Agilent Bond Elut Plexa solid phase extraction and electrospun polymer-silica composite sorbents for clean-up and preconcentration. Sample clean-up for alkaloids (hydrastine and berberine) in goldenseal, Hydrastis canadensis and flavonoids (quercetin, kaempferol and isorhamnetin) in Ginkgo biloba was achieved using Bond Elut Plexa SPE sorbent. Clean-up of flavonoids in Ginkgo biloba was also achieved using electrospun polymer-silica composite (polystyrene-silica, polyacrylonitrile-silica and nylon 6-silica) sorbents. All analysis of flavonoids and alkaloids was carried out using an Agilent 1200 Series HPLC coupled with a diode array detector. Good peak separation was achieved in less than 6 min employing an Agilent ZORBAX Eclipse Plus C18 column (4.6 x 75 mm, 3.5 μm) at 35⁰C. The mobile phases employed were 0.1% phosphoric acid/methanol gradient and 0.5% phosphoric acid/methanol (40:60) for alkaloids and flavonoids respectively. The calibration curves exhibited linearity up to 120 μg mL⁻¹ with correlation coefficients of more than 0.9980. The recoveries ranged from 73-109% with relative standard deviation of less than 5% for all analytes. Agilent Chem Elut supported liquid extraction was employed for the development of a sample preparation method for the determination of 24 banned aromatic amines from azo dyes in textile following the EU standard method EN 14362-1:2003 (E) and the Chinese standard method GB/T 17592-2006. The supported liquid extraction was effective in the extraction of the aromatic amines from textile (cotton, wool and polyester/cotton [80%:20%]). Most of the recoveries obtained were conforming to the minimum requirements set in the EN 14362-1:2003 (E) standard method and the relative standard deviations were less than 15%. Good peak separation was obtained within 70 min run time using the Agilent Zorbax SB-Phenyl column (4.6 mm x 250 mm, 5-micron) or the Agilent DB-35 MS (J & W) (30 m x 0.25 mm, 0.25 μm film thickness. It was demonstrated that the polymeric Agilent Bond Elut Plexa, electrospun nanofibers and diatomaceous earth were effective in extraction of alkaloids, flavonoids and aromatic amines in different matrices. The developed methods were simple, rapid and reproducible.
- Full Text:
- Date Issued: 2013
Polymer based electrospun nanofibers as diagnostic probes for the detection of toxic metal ions in water
- Authors: Ondigo, Dezzline Adhiambo
- Date: 2013
- Subjects: Heavy metals , Nanofibers , Nanoparticles , Colorimetric analysis
- Language: English
- Type: Thesis , Doctoral , PhD
- Identifier: vital:4557 , http://hdl.handle.net/10962/d1018261
- Description: The thesis presents the development of polymer based electrospun nanofibers as diagnostic probes for the selective detection of toxic metal ions in water. Through modification of the chemical characteristics of nanofibers by pre- and post-electrospinning treatments, three different diagnostic probes were successfully developed. These were the fluorescent pyridylazo-2-naphthol-poly(acrylic acid) nanofiber probe, the colorimetric probe based on glutathione-stabilized silver/copper alloy nanoparticles and the colorimetric probe based on 2-(2’-Pyridyl)-imidazole functionalized nanofibers. The probes were characterized by Fourier transform infrared spectroscopy (FTIR), Energy dispersive x-ray spectroscopy (EDX), Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM). The fluorescent nanofiber probe was developed towards the determination of Ni²⁺. Covalently functionalized pyridylazo-2-naphthol-poly(acrylic acid) polymeric nanofibers were employed. The solid state Ni²⁺ probe exhibited a good correlation between the fluorescence intensity and nickel concentration up to 1.0 mg/mL based on the Stern-Volmer mechanism. The detection limit of the nanofiber probe was found to be 0.07 ng/mL. The versatility of the fluorescent probe was demonstrated by affording a simple, rapid and selective detection of Ni²⁺ in the presence of other competing metal ions by direct analysis without employing any sample handling steps. For the second part of the study, a simple strategy based on the in-situ synthesis of the glutathione stabilized silver/copper alloy nanoparticles (Ag/Cu alloy NPs) in nylon 6 provided a fast procedure for fabricating a colorimetric probe for the detection of Ni²⁺ in water samples. The electrospun nanofiber composites responded to Ni²⁺ ions but did not suffer any interference from the other metal ions. The effect of Ni²⁺ concentration on the nanocomposite fibers was considered and the “eye-ball” limit of detection was found to be 5.8 μg/mL. Lastly, the third probe was developed by covalently linking an imidazole derivative; 2-(2′-Pyridyl)-imidazole (PIMH) to Poly(vinylbenzyl chloride) (PVBC) and nylon 6 nanofibers by post-electrospinning treatments using a wet chemical method and graft copolymerization technique, respectively. The post-electrospinning modifications of the nanofibers were achieved without altering their fibrous morphology. The color change to red-orange in the presence of Fe²⁺ for both the grafted nylon 6 (white) and the chemically modified PVBC (yellow) nanofibers was instantaneous. The developed diagnostic probes exhibited the desired selectivity towards the targeted metal ions.
- Full Text:
- Date Issued: 2013
- Authors: Ondigo, Dezzline Adhiambo
- Date: 2013
- Subjects: Heavy metals , Nanofibers , Nanoparticles , Colorimetric analysis
- Language: English
- Type: Thesis , Doctoral , PhD
- Identifier: vital:4557 , http://hdl.handle.net/10962/d1018261
- Description: The thesis presents the development of polymer based electrospun nanofibers as diagnostic probes for the selective detection of toxic metal ions in water. Through modification of the chemical characteristics of nanofibers by pre- and post-electrospinning treatments, three different diagnostic probes were successfully developed. These were the fluorescent pyridylazo-2-naphthol-poly(acrylic acid) nanofiber probe, the colorimetric probe based on glutathione-stabilized silver/copper alloy nanoparticles and the colorimetric probe based on 2-(2’-Pyridyl)-imidazole functionalized nanofibers. The probes were characterized by Fourier transform infrared spectroscopy (FTIR), Energy dispersive x-ray spectroscopy (EDX), Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM). The fluorescent nanofiber probe was developed towards the determination of Ni²⁺. Covalently functionalized pyridylazo-2-naphthol-poly(acrylic acid) polymeric nanofibers were employed. The solid state Ni²⁺ probe exhibited a good correlation between the fluorescence intensity and nickel concentration up to 1.0 mg/mL based on the Stern-Volmer mechanism. The detection limit of the nanofiber probe was found to be 0.07 ng/mL. The versatility of the fluorescent probe was demonstrated by affording a simple, rapid and selective detection of Ni²⁺ in the presence of other competing metal ions by direct analysis without employing any sample handling steps. For the second part of the study, a simple strategy based on the in-situ synthesis of the glutathione stabilized silver/copper alloy nanoparticles (Ag/Cu alloy NPs) in nylon 6 provided a fast procedure for fabricating a colorimetric probe for the detection of Ni²⁺ in water samples. The electrospun nanofiber composites responded to Ni²⁺ ions but did not suffer any interference from the other metal ions. The effect of Ni²⁺ concentration on the nanocomposite fibers was considered and the “eye-ball” limit of detection was found to be 5.8 μg/mL. Lastly, the third probe was developed by covalently linking an imidazole derivative; 2-(2′-Pyridyl)-imidazole (PIMH) to Poly(vinylbenzyl chloride) (PVBC) and nylon 6 nanofibers by post-electrospinning treatments using a wet chemical method and graft copolymerization technique, respectively. The post-electrospinning modifications of the nanofibers were achieved without altering their fibrous morphology. The color change to red-orange in the presence of Fe²⁺ for both the grafted nylon 6 (white) and the chemically modified PVBC (yellow) nanofibers was instantaneous. The developed diagnostic probes exhibited the desired selectivity towards the targeted metal ions.
- Full Text:
- Date Issued: 2013
The development of platinum and palladium-selective polymeric materials
- Authors: Fayemi, Omolola Esther
- Date: 2013 , 2013-05-03
- Subjects: Polymers , Platinum , Palladium , Adsorption , Sorbents , Nanofibers , Amines , Nanoparticles
- Language: English
- Type: Thesis , Masters , MSc
- Identifier: vital:4287 , http://hdl.handle.net/10962/d1002964 , Polymers , Platinum , Palladium , Adsorption , Sorbents , Nanofibers , Amines , Nanoparticles
- Description: The adsorption and separation of platinum(IV) and palladium(II) chlorido species (PtCl₆²⁻ and PdCl₄²⁻) on polystyrene-based beads and nanofibers as well as silica microparticles functionalized with polyamine centres derived from ethylenediamine (EDA), diethylenetriamine (DETA), triethylenetriamine (TETA) and tris-(2-aminoethyl)amine (TAEA) is described. The functionalized sorbent materials were characterized by using microanalysis, SEM, XPS, BET and FTIR. The nanofiber sorbent material functionalized with ethylenediamine (F-EDA) had the highest loading capacity which was attributed to its high nitrogen content (10.83%) and larger surface area (241.3m²/g). The adsorption and loading capacities of the sorption materials were investigated using both the batch and column studies in 1 M HCI. The adsorption studies for both PtCl₆²⁻ and PdCl₄²⁻ on the polystyrene-based sorbent materials fit the Langmuir isotherm while the silica-based sorbents fitted the Freundlich isotherm with R² values > 0.99. In the column experiment the highest loading capacity of Pt and Pd were 7.4 mg/g and 4.3 mg/g respectively on the nanofiber sorbent material based on ethylenediamine (EDA). The polystyrene and silica-based resins with triethylenetetramine (TETA) functionality (M-TETA and S-TETA) showed selectivity for platinum and palladium, respectively. Metal chlorido complexes loaded on the sorbent materials were recovered by using 3% m/v thiourea solution as teh eluting agent with quantitative desorption efficiency under the selected experimental conditions. The separation of platinum from palladium was partially achieved by selective stripping of PtCl₆²⁻ with 0.5 M of NaClO₄ in 1.0 M HCI with PdCl₄²⁻ was eluted with 0.5 M thiourea in 1.0 M HCI. The selectivity of the M-TETA and S-TETA sorbent materials was proved by column separation of platinum(IV) and palladium(II), respectively, from synthetic solutions containing iridium(IV) and rhodium(III). The loading capacity for platinum on M-TETA was 0.09 mg/g while it was 0.27 mg/g for palladium on S-TETA. , Acrobat PDFMaker 10.1 for Word , Adobe Acrobat 9.54 Paper Capture Plug-in
- Full Text:
- Date Issued: 2013
- Authors: Fayemi, Omolola Esther
- Date: 2013 , 2013-05-03
- Subjects: Polymers , Platinum , Palladium , Adsorption , Sorbents , Nanofibers , Amines , Nanoparticles
- Language: English
- Type: Thesis , Masters , MSc
- Identifier: vital:4287 , http://hdl.handle.net/10962/d1002964 , Polymers , Platinum , Palladium , Adsorption , Sorbents , Nanofibers , Amines , Nanoparticles
- Description: The adsorption and separation of platinum(IV) and palladium(II) chlorido species (PtCl₆²⁻ and PdCl₄²⁻) on polystyrene-based beads and nanofibers as well as silica microparticles functionalized with polyamine centres derived from ethylenediamine (EDA), diethylenetriamine (DETA), triethylenetriamine (TETA) and tris-(2-aminoethyl)amine (TAEA) is described. The functionalized sorbent materials were characterized by using microanalysis, SEM, XPS, BET and FTIR. The nanofiber sorbent material functionalized with ethylenediamine (F-EDA) had the highest loading capacity which was attributed to its high nitrogen content (10.83%) and larger surface area (241.3m²/g). The adsorption and loading capacities of the sorption materials were investigated using both the batch and column studies in 1 M HCI. The adsorption studies for both PtCl₆²⁻ and PdCl₄²⁻ on the polystyrene-based sorbent materials fit the Langmuir isotherm while the silica-based sorbents fitted the Freundlich isotherm with R² values > 0.99. In the column experiment the highest loading capacity of Pt and Pd were 7.4 mg/g and 4.3 mg/g respectively on the nanofiber sorbent material based on ethylenediamine (EDA). The polystyrene and silica-based resins with triethylenetetramine (TETA) functionality (M-TETA and S-TETA) showed selectivity for platinum and palladium, respectively. Metal chlorido complexes loaded on the sorbent materials were recovered by using 3% m/v thiourea solution as teh eluting agent with quantitative desorption efficiency under the selected experimental conditions. The separation of platinum from palladium was partially achieved by selective stripping of PtCl₆²⁻ with 0.5 M of NaClO₄ in 1.0 M HCI with PdCl₄²⁻ was eluted with 0.5 M thiourea in 1.0 M HCI. The selectivity of the M-TETA and S-TETA sorbent materials was proved by column separation of platinum(IV) and palladium(II), respectively, from synthetic solutions containing iridium(IV) and rhodium(III). The loading capacity for platinum on M-TETA was 0.09 mg/g while it was 0.27 mg/g for palladium on S-TETA. , Acrobat PDFMaker 10.1 for Word , Adobe Acrobat 9.54 Paper Capture Plug-in
- Full Text:
- Date Issued: 2013
- «
- ‹