- Title
- Characterisation of dissimilar friction stir welds between 5754 Aluminium alloy and C11000 copper
- Creator
- Akinlabi, Esther Titilayo
- Subject
- Friction stir welding
- Subject
- Aluminum alloys
- Subject
- Copper alloys
- Date Issued
- 2010
- Date
- 2010
- Type
- Thesis
- Type
- Doctoral
- Type
- DTech
- Identifier
- vital:9629
- Identifier
- http://hdl.handle.net/10948/1536
- Identifier
- Friction stir welding
- Identifier
- Aluminum alloys
- Identifier
- Copper alloys
- Description
- Friction Stir Welding (FSW) is a solid state welding process invented and patented by The Welding Institute (TWI) in 1991, for joining ferrous and non-ferrous materials1. The FSW of Aluminium and its alloys has been commercialised; and recent interest is focused on joining dissimilar materials. However, in order to commercialise the process, research studies are required to characterise and establish process windows. This research work through material characterisation of the welded joints establishes a process window for the Friction Stir welding of 5754 Aluminium Alloy and C11000 Copper. Furthermore, preliminary studies83,85 on the FSW of aluminium and copper have revealed the presence of intermetallic compounds which are detrimental to the weld qualities. This research work is also aimed at establishing process parameters that will result in limited or no intermetallic formation in the weld. The joint integrity of the resulting welds will also be correlated with the input process parameters. Based on the preliminary investigations conducted, a final weld matrix consisting of twenty seven welds was produced by varying the rotational speed between 600 and 1200 rpm, and the feed rate between 50 and 300 mm/min using three different shoulder diameter tools – 15, 18 and 25 mm to compare the heat input into the welds and to achieve the best results. The welds were characterised through microstructural evaluation, tensile testing, microhardness profiling, X-Ray Diffraction analysis, electrical resistivity and statistical analysis – in order to establish the interrelationship between the process parameters and the weld qualities. viii Microstructural evaluation of the weld samples revealed that the interfacial regions are characterised by mixture layers of aluminium and copper; while 33 percent of the tensile samples are within the acceptable range (> 75 percent joint efficiency). High Vickers microhardness values were measured at the joint interfaces, which corresponded with the intermetallic compounds. The Energy Dispersive Spectroscopy analysis revealed the presence of thin layers of intermetallics in nanoscale at the interfacial regions. The diffractograms of the X-Ray Diffraction analysis showed small peaks for intermetallics in some of the welds. Low electrical resistivities were measured at the joint interfaces. The statistical analysis showed that the downward vertical force, (Fz) can significantly influence the resulting weld qualities. An overall summary of the analysis of the weld qualities - with respect to the shoulder diameter tools employed showed that the 18 mm shoulder diameter tool is most appropriate among the three shoulder diameters considered, and a process window of medium spindle speed of 950 rpm and low-to-medium feed rate between 50 and 150 mm/min is established for FSW of Aluminium and Copper. Welds produced at 1200 rpm and 300 mm/min with low heat input did not have intermetallics formed at the joint interface.
- Format
- xxxi, 284 leaves
- Format
- Publisher
- Nelson Mandela Metropolitan University
- Publisher
- Faculty of Engineering, the Built Environment and Information Technology
- Language
- English
- Rights
- Nelson Mandela Metropolitan University
- Hits: 2227
- Visitors: 2374
- Downloads: 313
Thumbnail | File | Description | Size | Format | |||
---|---|---|---|---|---|---|---|
View Details Download | SOURCEPDF | 8 MB | Adobe Acrobat PDF | View Details Download |