F-and F+-band radioluminescence and the influence of annealing on its emission spectra in Al2O3: C, Mg:
- Chithambo, Makaiko L, Kalita, Jitumani M, Finch, A A
- Authors: Chithambo, Makaiko L , Kalita, Jitumani M , Finch, A A
- Date: 2020
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/150130 , vital:38942 , https://doi.org/10.1016/j.radmeas.2020.106306
- Description: Radioluminescence spectra of Al2O3:C,Mg monitored at temperatures up to 400 °C is reported. Measurements were made on samples either as received or on ones annealed at 1200 °C. Radioluminescence is observed at 410 nm for the unannealed sample but principally at 330 and 410 nm in the annealed sample with the emission at 330 nm dominant. Both bands are subject to thermal quenching but the change for the F+ band is atypical. Temperature induced effects on these and other bands are discussed, as are complementary measurements of thermoluminescence spectra.
- Full Text:
- Date Issued: 2020
- Authors: Chithambo, Makaiko L , Kalita, Jitumani M , Finch, A A
- Date: 2020
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/150130 , vital:38942 , https://doi.org/10.1016/j.radmeas.2020.106306
- Description: Radioluminescence spectra of Al2O3:C,Mg monitored at temperatures up to 400 °C is reported. Measurements were made on samples either as received or on ones annealed at 1200 °C. Radioluminescence is observed at 410 nm for the unannealed sample but principally at 330 and 410 nm in the annealed sample with the emission at 330 nm dominant. Both bands are subject to thermal quenching but the change for the F+ band is atypical. Temperature induced effects on these and other bands are discussed, as are complementary measurements of thermoluminescence spectra.
- Full Text:
- Date Issued: 2020
Thermoluminescence of SrAl2O4: Eu2+, Dy3+: kinetic analysis of a composite-peak
- Chithambo, Makaiko L, Wako, A H, Finch, A A
- Authors: Chithambo, Makaiko L , Wako, A H , Finch, A A
- Date: 2017
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/124157 , vital:35571 , https://doi.org/10.1016/j.radmeas.2016.12.009
- Description: The kinetic analysis of thermoluminescence of beta-irradiated SrAl2O4:Eu2+,Dy3+ is reported. The glow-curve is dominated by an apparently-single peak. It has been demonstrated using a number of tests including partial dynamic-heating, isothermal heating, phosphorescence and, the effect of fading, that the peak and the glow-curve consists of a set of closely-spaced peaks. In view of the peak being complex, its first few components were abstracted and analysed and for comparison, the peak was also analysed assuming it is genuinely single.
- Full Text: false
- Date Issued: 2017
- Authors: Chithambo, Makaiko L , Wako, A H , Finch, A A
- Date: 2017
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/124157 , vital:35571 , https://doi.org/10.1016/j.radmeas.2016.12.009
- Description: The kinetic analysis of thermoluminescence of beta-irradiated SrAl2O4:Eu2+,Dy3+ is reported. The glow-curve is dominated by an apparently-single peak. It has been demonstrated using a number of tests including partial dynamic-heating, isothermal heating, phosphorescence and, the effect of fading, that the peak and the glow-curve consists of a set of closely-spaced peaks. In view of the peak being complex, its first few components were abstracted and analysed and for comparison, the peak was also analysed assuming it is genuinely single.
- Full Text: false
- Date Issued: 2017
- «
- ‹
- 1
- ›
- »