Optically stimulated luminescence of ultra-high molecular weight polyethylene: a study of dosimetric features
- Authors: Chithambo, Makaiko L , Kalita, Jitumani M
- Date: 2018
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/110035 , vital:33217 , https://doi.org/10.1016/j.radmeas.2018.06.006
- Description: We report the dosimetric features of ultra-high molecular weight polyethylene (UHMWPE) using luminescence optically stimulated using 470 nm blue light. Samples irradiated to between 1 and 1000 Gy produces luminescence that increases with irradiation dose to produce a linear dose response between 1 and 1000 Gy. The sample was determined not to be affected by pre-dose in tests using a pre-dose of 4000 Gy. This characteristic precludes the need for elaborate background erasing routines typical of dosimetry experiments. The signal has good reproducibility. We used this property to test recovery of ‘unknown’ doses with encouraging results. It was observed that luminescence can also be stimulated using 870 nm infrared light. The dose response, fading, pre-dose effect and the ability to optically stimulate luminescence from the polymer is discussed in terms of curing involving free-radicals.
- Full Text: false
- Date Issued: 2018
Phototransferred thermoluminescence and thermally-assisted optically stimulated luminescence dosimetry using α-Al2O3:C,Mg annealed at 1200°C
- Authors: Kalita, Jitumani M , Chithambo, Makaiko L
- Date: 2018
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/105422 , vital:32511 , https://doi.org/10.1016/j.jlumin.2018.08.085
- Description: We report phototransferred thermoluminescence (PTTL) and thermally-assisted optically stimulated luminescence (TA-OSL) of α-Al2O3:C,Mg annealed at 1200 °C. PTTL is TL measured from an irradiated phosphor after its exposure to light. The other theme of this study, TA-OSL is the additional amount of luminescence optically stimulated from a sample over and above the amount that would be measured at room temperature. A sample irradiated to 10 Gy and preheated to 230 °C at 1 °C/s followed by illumination by 470 nm blue light produced four PTTL peaks at 53, 80, 102 and 173 °C. The PTTL peaks occur at the same positions as the corresponding conventional TL peaks. Their kinetic parameters are also similar. The intensity of the PTTL peaks increased with duration of illumination to a maximum within 200 s for doses between 1 Gy and 10 Gy. The dose response of each of the PTTL peaks at 80, 102 and 173 °C is linear within 1–15 Gy. The rate of fading is low and the peaks are reproducible. When the irradiated sample is optically stimulated at temperatures between 30 °C and 300 °C, after preheating to 500 °C, the intensity of its TA-OSL goes through a peak with temperature at 200 °C. Using the rising edge of the plot, activation energy of thermal assistance for a deep electron trap was estimated as (0.21 ± 0.02) eV. The TA-OSL dose response is sublinear from 10–250 Gy and saturates thereafter. The PTTL and TA-OSL analyses signify that the concentration of deep traps in α-Al2O3:C,Mg increased after annealing at 1200 °C. As a result, the sample produced better PTTL and TA-OSL response than when annealed at lower temperature.
- Full Text: false
- Date Issued: 2018
Phototransferred thermoluminescence of synthetic quartz: analysis of illumination-time response curves
- Authors: Chithambo, Makaiko L , Niyonzima, P , Kalita, Jitumani M
- Date: 2018
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/111020 , vital:33364 , https://doi.org/10.1016/j.jlumin.2018.02.029
- Description: Phototransferred thermoluminescence (PTTL) induced in synthetic quartz by 470 nm blue light is reported. The glow curve measured at 5 °C/s up to 500 °C after irradiation to 100 Gy shows six peaks at 94, 116, 175, 212, 280 and 348 °C labelled I through VI and another one at 80 °C (labelled A1). PTTL is only observed for peaks A1 and I and is induced at peak A1 as long as peak III has been removed by preheating and at peak I after preheating to deplete peak VI. The inducement of PTTL even when all peaks have been removed points to deep electron traps in the quartz also acting as donors in addition to the putative ones below 500 °C. The PTTL intensity as a function of duration of illumination for A1 goes through a peak and decreases monotonically or to a stable value depending on the preheating temperature. The change of PTTL intensity as a function of illumination time is described using a set of coupled linear differential equations. The number of acceptors and donors in a particular system described in this way is influenced by the preheating temperature.
- Full Text: false
- Date Issued: 2018
The effect of annealing and beta irradiation on thermoluminescence spectra of α-Al2O3: C, Mg
- Authors: Kalita, Jitumani M , Chithambo, Makaiko L
- Date: 2018
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/112875 , vital:33669 , https://doi.org/10.1016/j.jlumin.2017.12.036
- Description: The effect of annealing on thermoluminescence spectra of beta irradiated α-Al2O3:C,Mg has been studied. Measurements were made on an un-annealed sample and samples annealed at 600, 700 and 900 °C. A glow curve measured at 1 °C/s from samples irradiated to 1 Gy shows a high intensity peak at 163 °C and six secondary peaks of weaker intensity at 43, 73, 195, 280, 329 and 370 °C. When the samples are annealed at 700 or 900 °C, an additional secondary peak appears at 100 °C. The thermoluminescence spectrum of an un-annealed sample measured at 1 °C/s between 300 and 700 nm shows the main emission band at ~ 410 nm and subsidiary emission bands at ~ 325 and 485 nm. The emission from samples annealed at 700 and 900 °C show similar bands except for a decrease in intensity of the emission at 485 nm. The emission bands at 325, 410 and 485 nm are attributed to F+, F and F22+(2Mg) -centres respectively. The decrease of the emission band at 485 nm is deduced to be due to the destruction of the F22+(2Mg) centre at 700 °C. The emission bands are unaffected by irradiation dose between 10 and 320 Gy. However, when the sample is annealed at or beyond 700 °C, any effects on the F+ and F centres emission can be easier distinguished particularly for doses greater than 10 Gy.
- Full Text: false
- Date Issued: 2018
The effect of pre-dose on thermally and optically stimulated luminescence from α-Al2O3C, Mg and α-Al2O3: C
- Authors: Kalita, Jitumani M , Chithambo, Makaiko L
- Date: 2018
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/111011 , vital:33363 , https://doi.org/10.1016/j.apradiso.2018.06.012
- Description: We report the effect of pre-dose on the thermoluminescence (TL) and optically stimulated luminescence (OSL) dose response of α-Al2O3:C,Mg and α-Al2O3:C. Before any luminescence measurement, the samples were irradiated with different doses, namely 100, 500 and 1000 Gy to populate the deep electron traps. This is the pre-dose. The results from TL and OSL studies are compared with results from samples used without any pre-measurement dose. The TL glow curves and OSL decay curves of α-Al2O3:C,Mg recorded after pre-doses of 100, 500 and 1000 Gy are identical to those from a sample used without any pre-dose. Further, the TL and OSL dose response of all α-Al2O3:C,Mg samples are similar regardless of pre-dose. In comparison, the TL glow curves and OSL decay curves of α-Al2O3:C are influenced by pre-dose. We conclude that the differences in the TL and OSL dose response of various pre-dosed samples of α-Al2O3:C are due to the concentration of charge in the deep traps. On the other hand, owing to the lower concentration of such deep traps in α-Al2O3:C,Mg, the TL or OSL dose responses are not affected by pre-dose in this material.
- Full Text: false
- Date Issued: 2018
Thermoluminescence of α-Al2O3: C, Mg annealed at 1200° C
- Authors: Kalita, Jitumani M , Chithambo, Makaiko L
- Date: 2018
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/111030 , vital:33365 , https://doi.org/10.1016/j.nimb.2018.03.003
- Description: Stimulated luminescence in α-Al2O3:C,Mg has thus far been studied for samples annealed at temperature no higher than 900 °C as can be seen by an examination of the literature. We report the thermoluminescence (TL) features of α-Al2O3:C,Mg annealed at 1200 °C. A glow curve measured at 1 °C/s from the samples annealed at 1200 °C shows eight peaks at 54, 80, 102, 173, 238, 290, 330 and 387 °C. Kinetic analyses show that the peak at 54 °C follows general order kinetics (b = 1.3) whereas the rest follow first order kinetics. The values of the activation energy of the peaks are between 0.77 eV and 1.90 eV and the frequency factors are of the order of 1010–1014 s−1. The intensity of the peaks at 54, 80, 102 and 173 °C increase with heating rate whereas those of the peaks at 238 and 290 °C decrease with heating rate. The decrease of intensity of the peaks at 238 and 290 °C with heating rate is due to thermal quenching whereas the increase of intensity of the peaks with heating rate indicates an inverse thermal-quenching-like behaviour. Interestingly this behaviour is observed only after annealing at 1200 °C. The activation energy for thermal quenching as calculated using the peaks at 238 and 290 °C are (1.02 ± 0.16) eV and (1.33 ± 0.15) eV respectively. Regarding the dosimetric features, the dose response of the peaks at 54, 80 and 102 °C are sublinear within 1–10 Gy and the peak at 54 °C saturates above 6 Gy. In contrast, the response of the peak at 173 °C is sublinear with 1–4 Gy and superlinear between 4 and 10 Gy. The peaks are found to fade at different rates and the rate of fading is also affected by annealing.
- Full Text: false
- Date Issued: 2018