- Title
- Potential use of carbon nanotubes as a nanofiller for natural rubber latex condoms
- Creator
- Agbakoba, Victor Chike
- Subject
- Nanotubes
- Subject
- Rubber chemistry Nanocomposites (Materials) Nanostructured materials
- Date Issued
- 2018
- Date
- 2018
- Type
- Thesis
- Type
- Masters
- Type
- MSc
- Identifier
- http://hdl.handle.net/10948/23393
- Identifier
- vital:30538
- Description
- The recent advancement in the field of nano-technology has raised much interest in the area of natural rubber latex (NRL) processing. This interest stems from the exceptional properties of nano-material and the promising results obtained by several researchers. Studies have shown that very low loadings of inorganic nanomaterials such as carbon nanotube (CNT) in NRL matrix leads to enhanced tensile strength, tensile modulus, tear resistance and aberration resistance. Thus providing a great prospect for reinforcement of thin film NRL articles such as condom. In this research, prevulcanised natural rubber latex (PvNRL) composite blends containing single walled carbon nanotubes (SWCNTs) were prepared via direct mixing. A progressive discolouration of PvNRL was observed with increased loadings of CNTs. Thermal analysis revealed faster drying rates for the composite blends containing SWCNT. Results from equilibrium swelling experiments also suggested a slight increase in crosslink density in the presence of SWCNT. There was a significant influence on flow behaviour of PvNRL as a result of varying loadings of SWCNT suspension. This was reflected as a change in pseudoplasticity and apparent viscosity. For Instance, apparent viscosity at a shear rate of 1 s-1 at 25°C for PvNRL with ~0.08% SWCNT was 2.5 Pa.s, compared to 0.49 Pa.s for the blends with 0.02% SWCNT. Condoms were moulded via the straight dipping technique using custom made glass formers. A series of dilutions was performed to correct the viscosity differences. This also ensured good consistency and promoted uniform deposition of PvNRL on the glass former. The average dimensions of the condoms produced in terms of length and width were ~191.17 ± 5.17 mm and 52.67 ± 5.17 mm respectively. Thickness measurement varied slightly according to the method of determination. The water leakage test suggested the absence of holes in the condoms produced. However, results from electrical leakage test contradicted those from water leak test. The results from infrared spectroscopy (FTIR) did not confirm the presence of chemical interactions between the SWCNT and PvNRL matrix. Glass transition temperature (Tg) was also unaffected across the blends. The stiffness (or modulus) was unaffected in all the condoms, as revealed by results from indentation hardness analysis. The SWCNT showed no significant influence on thermal decomposition temperatures of the condoms. Nonetheless, images from optical microscopy revealed increased surface roughness corresponding to higher loadings of SWCNT. Results from stress relaxation studies revealed improved retention of modulus under constant strain for condom samples containing SWCNT.
- Format
- xvii, 134 leaves
- Format
- Publisher
- Nelson Mandela University
- Publisher
- Faculty of Science
- Language
- English
- Rights
- Nelson Mandela University
- Hits: 1318
- Visitors: 1561
- Downloads: 289
Thumbnail | File | Description | Size | Format | |||
---|---|---|---|---|---|---|---|
View Details Download | SOURCE1 | Potential use of carbon nanotubes as a nanofiller for natural rubber latex condoms | 3 MB | Adobe Acrobat PDF | View Details Download |