- Microstructural based creep life assessment of 1CrMov Turbine rotor steels after long-term service
- Creator
- Nyembe, Hlanganani Siphelele
- Subject
- Materials – Creep –South Africa
- Subject
- Steel -- Creep
- Date Issued
- 2023-04
- Date
- 2023-04
- Type
- Doctoral theses
- Type
- text
- Identifier
- http://hdl.handle.net/10948/61380
- Identifier
- vital:70622
- Description
- Creep-resistant 1CrMoV steels are used for high-pressure turbine rotors in fossil fuel power stations operating at steam temperatures up to 565 °C in the creep regime. The upper bainitic microstructure of 1CrMoV rotors changes when exposed to high temperature service over long periods. The aim of this study was to relate these microstructural changes for service exposed 1CrMoV rotor steels to the remaining creep life as determined using existing methods. Analytical electron microscopy was used to quantitatively study the microstructural evolution of service-exposed 1CrMoV steel rotors. 1CrMoV rotor steel samples were characterised in the initial state, and three long-term (272 h to 300 kh) service exposed states. Detailed microstructural investigations were conducted to analyse the cavities; bainitic laths and packets; dislocations; carbide phases and their size, population, composition. The creep life fractions were estimated using conventional life assessment methods based on creep cavitation and hardness. The creep life fraction consumed of the rotors, estimated based on the creep cavities and hardness data, ranged from ~0.5 to 1. Electron backscattered diffraction (EBSD) was used to analyse the bainitic packets, laths, misorientations, and dislocations, which showed that the bainitic lath surface area to volume (SV) correlated with service time. The precipitates were extracted from the Fe-matrix using extraction replication and were further investigated using transmission Kikuchi diffraction (TKD), scanning transmission electron microscopy (STEM), selected area electron diffraction (SAED), and energy dispersive spectroscopy (EDS). STEM-EDS and TKD identified M3C, MC, M2C, M7C3, and M23C6 (M = Fe, Cr, Mo, V, Mn) in the 1CrMoV steels. STEM-EDS measurements revealed that Fe/Cr ratios in M3C decreased from 4.5 (initial state) to 2.5 (>272 kh). The Fe/Cr and Fe/Mo ratios in overall carbides decreased from 5 and 10 (initial state) to 1 and 2 (>272 kh), respectively. The TKD analysis indicated that the relative phase proportion of M2C and M7C3 carbides, relative to the total extracted carbides, is positively correlated with service exposure. These microstructural features correlate with the creep life fraction consumed and could potentially be used as another indicator of the remnant creep life.
- Description
- Thesis (PhD) -- Faculty of Science, School of Computer Science, Mathematics, Physics and Statistics. 2023
- Format
- computer
- Format
- online resource
- Format
- application/pdf
- Format
- 1 online resource (174 pages)
- Format
- Publisher
- Nelson Mandela University
- Publisher
- Faculty of Science
- Language
- English
- Rights
- Nelson Mandela University
- Rights
- All Rights Reserved
- Rights
- Open Access
- Hits: 103
- Visitors: 110
- Downloads: 14
| Thumbnail | File | Description | Size | Format | |||
|---|---|---|---|---|---|---|---|
| View Details Download | SOURCE1 | Nyembe, HS (1).pdf | 14 MB | Adobe Acrobat PDF | View Details Download |